tpo waterproof coiled material

tpo waterproof coiled material

thermoplastic polyolefin tpo is a waterproof membrane. its raw material is polymer and can be reinforced with polyester mesh and with fabric backing manufactured by advanced extrusion machining technology.

loading port payment termstt or lc min order qty

details

product overview

thermoplastic polyolefin tpo is a waterproof membrane. its raw material is polymer and can be reinforced with polyester mesh and with fabric backing manufactured by advanced extrusion machining technology.

product specifiion

product name product code thickness mm width mm length mm waterproofing sheets with internally reinforced with fabric p

1.21.5

10002000

2000025000

waterproofing sheets backed with fabric l 2000 homogeneous waterproofing sheets h 2000

product features

1. it is easy to install with good system integrity few accessories.

2. excellent tensile strength tearing resistance and penetration resistance performance.

3. no plasticizer. they have been tested as having excellent resistance to thermal aging and ultraviolet durable and exposed.

4. hot-air welding. the peel strength of joint is high.

5. fast welding speed.

6. environment friendly 100 recycled without chlorine.

7. durable hot welding performance and easy to repair.

8. smooth surface no fading and pollution.

appliion scope

widely applied on various kinds of waterproofing projects

1. subways and tunnels

2. roofs of sports complex

3. green roofs

4. exposed roofs

5. steel roofs

6. waste land filling yards

performance index

item

unit

value

h l p

resin thickness on middle mesh ge

mm

--

0.4

tensile properties

max. strength ge n/cm -- 200 250 tensile strength ge mpa 12.0 -- -- elongation at max. strength ge -- -- 15 breaking elongation ge 500 250 --

dimensional stability after heat treatment le

2.0 1.0 0.5

foldability at low temperature

-40℃ no cracks

water tightness

0.3mpa 2h no penetration

resistance to impact

0.5kgm no penetration

resistance to static loading

-- -- 20kgs no penetration

joint peel strengthge

n/mm

4.0 or membrane broken

3.0

right angle tearing strengthge

n/mm 60 -- --

trapezoid tearing strengthge

n -- 250 450

water absorption 70℃ 168h

4.0

aging in hot weather

115℃

time h

672

appearance

no bubbles cracks layering sticky holes

max. tensile retention rate ge -- 90 90 tensile strength retention rate ge 90 -- -- elongation retention rate at max. tensile ge -- -- 90 breaking elongation retention ratege 90 90 -- low temperature flexibility

-40℃ no cracks

chemical resistance

appearance

no bubbles cracks layering sticky holes

max. tensile retention rate ge -- 90 90 tensile strength retention rate ge 90 -- -- elongation retention rate at max. tensile ge -- -- 90 breaking elongation retention rate 90 90 -- low temperature flexibility

-40℃ no cracks

artificial aging

time

1500h

appearance

no bubbles cracks layering sticky holes

max. tensile retention rate ge -- 90 90 tensile strength retention rate ge 90 -- -- elongation retention rate at max. tensile ge -- -- 90 breaking elongation retention rate 90 90 -- low temperature flexibility

-40℃nocracks